Silicone Gels

Silicone Gels are two component (1:1 mix ratio) platinum curing materials that cure to a very soft gel like consistency. These products are used for protecting extremely delicate components from vibration and mechanical shock, as well as keeping them safe from water and atmospheric contaminants.

Silicone gels are used to provide protection from vibration, thermal or mechanical shock. Silicone gels also provide excellent moisture protection. Quantum Silicones' QGel product line consists of two component materials with a 1:1 mix ratio. Gels should be stored in the original unopened container at 25C (77F). They will remain useful for a period of 12 months if stored under those conditions.

Product	Description	Penetration	Viscosity	Cure system
QGel 300	High strength silicone gel	5-9	1000	30 min @ 150C
QGel 300Y	Yellow, soft, high strength silicone gel	5-9	1500	24h @ RT or 30 min @ 150C
QGel 301	High strength silicone gel	5-9	1000	24h @ RT
QGel 310	General purpose silicone gel	5-9	1000	30 min @ 150C
QGel 311	Rapid cure silicone gel	5-9	1000	5 min @ 150C
QGel 312	Clear, soft, tough, moderately cross-linked silicone polymer	19.5gram - 1.5mm 69.5gram - 6.5mm	1000	30 min @ 150C 60 min @ 100 24 hours @ 25
QGel 315	Extended pot life silicone gel	5-9	1100	15-30 min @ 150C
QGel 317	Fast curing, very soft silicone gel	12-20	1000	5 min @ 150C
QGel 318	Translucent, hard, tough, moderately cross-linked silicone polymer	3-8	150,000	30 min @ 150C 60 min @ 100C
QGel 322Y	Yellow, very soft, moderately cross-linked silicone polymer	4-8	750	20 minutes @ 150C 60 minutes @ 100C 24 hours @ 25C
QGel 323	Soft, tough, moderately cross-linked silicone gel.	19.5gram - 1.5mm 69.5gram - 6.5mm	5000	30 min @ 150C
QGel 324	Clear, very soft, moderately cross-linked silicone polymer	4-9	3000	24 hours @ RT
QGel 900	Clear, very soft, tough, moderately cross-linked silicone polymer. Refractive Index: 1.43	5-9	500	30 min @ 150C 60 min @ 100C 24 hours @ 25C
QGel 910	Clear, very soft, tough, moderately cross-linked silicone polymeric elastomer. Refractive Index: 1.47	5-9	500	30 min @ 150C 60 min @ 100C 24 hours @ 25C
QGel 920	Clear, very soft, tough, moderately cross-linked silicone polymeric elastomer	5-9	1500	30 min @ 150C 60 min @ 100C 24 hours @ 25C
Tuf-Gel 330	Clear, tough, moderately cross-linked gel	Shore 00: 30-50	700	30 min @ 150C
Tuf-Gel 331	Blue-tinted, clear, tough, moderately cross-linked gel	Shore 00: 30-50	700	30 min @ 150C